Lets start with a fresher on general Component Fatigue.

  • Fatigue occurs when a material is subjected to repeated loading and unloading.
  • When the loads are above a certain threshold, microscopic cracks will begin to form at a material’s surface.
  • Cracks always begin in high stressed areas of a material.
  • Eventually a crack will reach a critical size, and the structure will suddenly fracture.

In our prior blog on Fatigue we discussed the various cyclical loading applications. Let’s review them again with this graphic.

Now let’s get a little bit more specific and discuss the basic characteristics of Gear fatigue. Some of these basics are:

  • They always have an origin(s)
  • Progression marks may be visually present (depends on load variations)
  • They will have a Final Fracture Zone (FFZ)
  • Ratchet marks may be present
  • Spalls (or Hertzian Fatigue), may be present
  • Electrical fluting may be present
  • Evidence of inadequate lubrication may be present

Let’s run through some failed parts and see if we can associate these characteristics to them.

(1) This gear is heavily damaged at the addendum or top. The origin is Hertzian (beneath the surface working outward). Once the wear is through the case hardened area, the failure will be rapid.

Reliability Center

(2) This crack was initiated in the gear root and was under normal loads.

(3) The crack was initiated in the gear root and was under heavy loads because of the large FFZ.

Reliability Center

(4) The crack was initiated in the gear root where the stresses are high.

Reliability Center

(5) This gear is damaged at the addendum or top. The origin is Hertzian (beneath the surface working outward). This defect is often a result of misalignment.

Reliability Center

(6) This gear is also damaged at the addendum or top. The origin is Hertzian (beneath the surface working outward). This defect is often a result of misalignment.

Reliability Center

Just as an FYI, I am pulling all of this material from our public workshops as usual. These workshops appeal to the novice as well as the more seasoned investigators who just want to learn more about the physics of failure, recognizing common failure patterns and understanding how those patterns came to form.

As always, I appreciate all of the great feedback and sharing from the veterans in the field, and equally as important, the front-lines who make things happen!! Thank you for your time and participation.

Learn more about Why Parts Fail.

 

 

Related Articles

Sulzer Cost effective sustainable fuel production

Cost effective sustainable fuel production

Benchmarking Market Report highlights cost-leadership of Sulzer Chemtech BioFlux Process Technology for Renewable Fuels production BioFlux® process technology for renewable fuel…

Related Whitepapers

Expansion Joint Expertise Improves Industrial Wastewater System Reliability

The majority of industries have wastewater treatment plants. Government agencies and local governments require these facilities to meet pretreatment requirements. Pretreatment rules were enacted to prevent…

How to Decrease Oil Changes with Bearing Isolators [Inforgraphic]

Learning how to decrease oil changes can be time- and money-saving. Oil life can be long if contamination is eliminated, which is easier said than…

Synchronous Machines Are The Optimal Choice For Heavy Industry

TECO-Westinghouse experience assures superior performance and reliability For over a century, Westinghouse has been the pacesetter in the design and production of electric machines for heavy…

Why FLEXXORs Are Designed Differently

J. Hilbert Anderson, President of Coupling Corporation of America, discusses some of the reasons why FLEXXORs are designed differently from all other flexible couplings, and…

Comments

Leave a Reply

Your email address will not be published. Required fields are marked *

Join the #PumpTalk Community


By submitting this form, you are consenting to receive marketing emails from: Empowering Pumps & Equipment, 2205-C 7th Street, Tuscaloosa, AL, 35401, http://www.empoweringpumps.com. You can revoke your consent to receive emails at any time by using the SafeUnsubscribe® link, found at the bottom of every email. Emails are serviced by Constant Contact